| Conc.(%) | Temp.Deg C | Resistance | | ACETIC ACID, Glacial C.P. | 99 | 23 | PR | | ACETIC ACID, (aquepus) | 25 | 60 | R | | | 50 | 60 | R | | ACRYLONITRILE | 100 | 20 | R | | | 100 | 60 | R | | ACETONE | 100 | 23 | NR | | AMMONIA | 35 | 23 | R | | ALLYL BROMIDE | 100 | 23 | NR | | AMMONIUM CHLORIDE | 10 | 40 | R | | | 10 | 60 | R | | | Sat. | 60 | R | | AMMONIUM SULFATEX | 10 | 40 | R | | | 10 | 60 | R | | | Sat. | 60 | R | | AMMONIUM SULFIDE | 35 | 23 | PR | | AMMONIUM THIOGLYCOLATE | 100 | 23 | R | | 2-AMY CINNAMIC ALDEHYDE | 100 | 23 | NR | | BENZENE | 100 | 20 | PR | *** | | 100 | 60 | NR | *** | BENZOCYANAMIDE | 100 | 23 | | | BENZOTRICHLORIDE | 100 | 23 | NR | *** | 2-BROMO PYRIDINE | 100 | 23 | NR | | CALCIUM CHLORIDE | 10 | 20 | R | | | 10 | 60 | R | | | Sat. | 60 | R | | CALCIUM THIOCYANATE | 60 | 23 | R | | CARBON TETRACHLORIDE | 100 | 23 | NR | *** | CHROMIC ACID | 25 | 20 | R | | (aqueous) | 25 | 60 | R | | | 80 | 20 | R | | | 80 | 60 | R | | CITRIC ACID | 10 | 40 | R | | (aqueous) | 10 | 60 | R | | | Sat. | 60 | R | | CREOSOTE | 100 | 23 | NR | *** | (Hardwood) | | | | | CYCLOHEXINOL | 100 | 20 | R | | | 100 | 60 | R | | DETERGENT | 100 | 20 | R | | (Liquid) | 100 | 60 | R | | DIESEL OIL | 100 | 20 | R | | | 100 | 60 | PR | *** | ETHYL ACETATE | 100 | 22 | PR | | ETHYL ALCOHOL | 95 | 23 | PR | | ETHYLENE DICHLORIDE | 100 | 23 | NR | *** | ETHYLENE GLYCOL | 100 | 20 | R | | | 100 | 60 | R | | FORMALDEHYDE | 40 | 20 | R | | | 40 | 60 | R | | FORMIC ACID | 90 | 23 | PR | | GASOLINE | 100 | 23 | NR | *** | GUAICOL | 100 | 23 | NR | *** | GLYCERINE | 100 | 20 | R | | | 100 | 60 | R | | HYDROCHLORIC ACID C.P. | 20 | 23 | R | | | 26 | 23 | R | | | 30 | 20 | R | | | 31 | 23 | R | | | 38 | 23 | PR | | | 43 | 20 | PR | | | 43 | 60 | NR | | HYDRIODIC ACID | 45 | 23 | R | | HEPTANE | 100 | 23 | NR | *** | HYDROGEN PEROXIDE | 20 | 20 | R | | | 20 | 60 | R | | | 30 | 20 | R | | | 30 | 60 | R | | | 90 | 20 | R | | Amflex Plastics Inc | 90 | 60 | NR | |
| | Conc.(%) | Temp.Deg C | Resistance | | ISOPROPANAL | 100 | 20 | R | | | 100 | 60 | R | | KEROSENE | 100 | 23 | NR | * | LACTIC ACID | 10 | 20 | R | | | 10 | 60 | R | | METAL CUTTING OILS | 100 | 20 | R | | | 100 | 60 | PR | | MINERAL OIL | | | | | METHYL ETHYL KETONE | 100 | 23 | NR | | MOTOR OIL SAE 20 | 100 | 20 | R | | | 100 | 23 | R | | NAPTHA | 100 | 20 | R | | | 100 | 60 | PR | *** | NICOTINE ETHYL AMID | 100 | 23 | PR | | NICKEL SULFATE | 10 | 40 | R | | | 10 | 60 | R | | | Sat. | 60 | R | | NITRIC ACID C.P. | 30 | 20 | R | | | 30 | 60 | R | | | 50 | 20 | R | | | 67 | 23 | PR | | | 95 | 23 | NR(d) | | OLEIC ACID | Sat. | 30 | R | | | Sat. | 60 | PR | | PARALDEHYDE U.S.P. | 100 | 23 | NR | | PERCHLORIC ACID | 70 | 23 | PR | | | 60 | 23 | R | | PERACETIC ACID | 50 | 20 | NR | | PHENOL | 100 | 20 | R | | | 100 | 60 | R(d) | | PHENYL ISOCYANATE | 100 | 23 | NR | | PHOSPHORIC ACID | 85 | 23 | R | | POTASSIUM CYANIDE | 10 | 60 | R | | | Sat. | 60 | R | | SODIUM CHLORIDE | 10 | 20 | R | | (Table Salt) | 10 | 60 | R | | | Sat. | 60 | R | | SODIUM HYPOCHLORITE | 12 | 23 | R | | SODIUM HYDROXIDE | 30 | 20 | R | | | 30 | 60 | R | | | 50 | 20 | R | | | 50 | 60 | R | | SULFURIC ACID C.P. | 3 | 23 | R | | | 30 | 23 | R | | | 35 | 23 | R | | | 78-98 | 23-60 | NR | | SULFUROUS ACID | 6 | 23 | R | | SUGAR SYRUP | 50 | 20 | R | | | 50 | 60 | R | | TOLUENE | 100 | 23 | NR | *** | TRICHLORETHYLENE | 50 | 23 | NR | *** | TURPENTINE | 12 | 23 | NR | *** | UREA | 10 | 40 | R | | (Aqueus) | 10 | 60 | R | | | 33 | 60 | R | | VEGETABLE OIL | | | | *** |
(R) RESISTANT 2.5% Change in weight or swell (PR) PARTIALLY RESISTANT 2.5 - 7% Change in weight or swell (NR) NOT RESISTANT 7% Change in weight or swell (d) SAMPLE DISCOLORS These values are obtained from laboratory prepared specimens and may not be exactly duplicated in commercial practice. |